POM 107.doc

名称规格: POM 107 产地: 美国杜邦特性: 一般级提供方:东莞金橙塑胶TEL:152 /076 9/2 620①原料描述部分规格级别: 注塑级外观颜色: --- 用途概述: --- 备注说明: 特性:均聚甲醛,强度、刚度、热稳定性能好、硬度好。②原料技术数据性能项目试验条件[状态]测试方法测试数据数据单位其它性能弯曲降服强度+73 ?HASTM D-790 MPsi 基本性能密度---ASTM D-792 --- 物理性能吸水量 24hrs 浸泡+73 ?H(+23 ℃)ASTM D-570 % 吸水量 %.+73 ?H(+23 ℃)ASTM D-570 % 吸水量浸泡均衡点+73 ?H(+23 ℃)ASTM D-570 % 扩散因数+73 ?H(+23 ℃)10 6HzASTM D-150 --- 机械性能洛氏硬度---ASTM D-785 M94,R12 0 --- 摩擦+73 ?H(+23 ℃)静态 ThrustWasherTest --- 系数摩擦系数+73 ?H(+23 ℃)动态 ThrustWasherTest --- 挠曲系数+122 ℃在25℃下620 MPa 弯曲降服强度+23 ℃ASTM D-790 MPa 压缩应力+73 ?******@1%Def. ASTM D-695 MPsi 挠曲系数+70 ℃在25℃下1550 MPa 挠曲系数+212 ?H在25℃下130 MPsi 挠曲系数+100 ℃25℃下895 MPa 挠曲系数+250 ?H在25℃下90MPsi 弹性系数+23 ℃ASTM D-638 3100 MPa 剪力+73 ?HASTM D-732 MPsi 剪+23 ℃ASTM D-732 MPa 力挠曲系数-68 ?H在25℃下530 MPsi 挠曲系数-55 ℃在25℃下3650 MPa 挠曲系数+73 ?H在25℃下380 MPsi 挠曲系数+23 ℃在25℃下2620 MPa 挠曲系数+158 ?H在25℃下225 MPsi 断裂时之拉力伸张度-68 ?H(-55 ℃)ASTM D-638 38% 断裂时之拉力伸张度+73 ?H(+23 ℃)ASTM D-638 75% 断裂时之+158 ?H(+70 ℃)ASTM D-638 230 % 拉力伸张度断裂时之拉力伸张度+212 ?H(+100 ℃)ASTM D-638 >260 % 断裂时之拉力伸张度+250 ?H(+122 ℃)ASTM D-638 >260 % 伸张强度-68 ?HASTM D-638 MPsi 伸张强度-55 ℃ASTM D-638 101 MPa 伸张强度+73 ?HASTM D-638 MPsi 伸张强度+23 ℃ASTM D-638 MPa 伸张强度+158 ?HASTM D-638 MPsi 伸张强度+70 ℃ASTM D-638 MPa 伸张强度+212 ?HASTM D-638 MPsi 伸张强度+250 ?HASTM D-638 MPsi 伸张强度+122 ℃ASTM D-638 MPa 伸张强度+100 ℃AST