8自硬树脂砂增强剂的研究与应用
树脂增强剂在自硬树脂砂中的应用研究
东风汽车公司通用铸锻厂马朝阳
摘要:本文研究在自硬树脂中加入增强剂以提高树脂砂强度,降低树脂加入量。在实验室对KH550、
G-439两种增强剂,新砂、再生砂两种砂,在两种树脂上进行了试验,结果表明KH550和G-439均有一定的增强效果,并找到了最佳加入量,在生产上进行了试用,具有较好的效果。关键词:自硬树脂砂增强剂对比试验
A Stuty of Resin Strengthener user in Self-setting Resin Sand
Ma Chaoyang(General Foundry and Forging Plant, Dongfeng Motor Co.)
Abstract This paper is the study of strengthener in self-setting resin for increasing resin addition. Tests were carried out for -439 strengtheners and for new sand and reclaimed sand, which showed good strengthening results and their optimum additions were also found. They have been applied in production effectively.
Keywords Self-setting resin sand parison test
1 前言
随着自硬树脂砂工艺在我厂的广泛应用,价格昂贵的树脂消耗量日益增加,尽管树脂砂工艺有许多优越性,但成本高日益困扰着树脂砂工艺的发展,如何降低树脂消耗,成为广大铸造工作者关心的问题。
就树脂砂而言,降低树脂加入量通常有两种途径:一是选用优质原材料。原砂选用粒形圆整、含泥量低的擦洗砂,树脂选用比强度高、质量稳定的树脂。二是在树脂中加入增强剂提高树脂与砂粒间的粘结力。由于地理位置所限,原砂只能选用粒形较差的湖南砂,%才能满足工艺要求,与相比尚有一定的差距。因此在树脂中加入增强剂以提高树脂砂强度、降低树脂加入量成为迫切需要探讨的问题。
2 增强剂的选择
有机硅烷增强剂
目前通常使用的是:γ-氨基丙基三乙氧基硅烷(分子式:H2N(CH2)Si(OC2H5)3 ,国外牌号A1100,国内牌号KH550),γ-缩水甘油醚丙基三甲硅烷(国外牌号A187,国内牌号KH560),甲基丙烯酸次丙基三甲氧基硅烷,以及某化工厂生产的G-439(分子式:R-N〔(CH2)3Si(OC2H5)〕2)。
1
上述产品中,KH550对呋喃树脂增强效果最好,但价格较高(180元/kg),而G-439虽效果不如KH550,但其价格较低(50元/kg),因此我们对KH550和G-439进行了对比试验。
有机硅烷增强剂的增强机理
国内外的研究表明:树脂砂型芯的断裂,主要是混合断裂和附着断裂,即由树脂膜与砂粒间的附着力所决定的。鉴于原砂的表面状态和性质,一般情况下,树脂膜-砂粒界面间的附着力远