Abstract:The effect of retarders, the dosage of steel slag on the properties of alkaliactivated steel slagslag based cementitious materials and the hydration characteristics of plex binding material ination of strength and hydration heat evolution as icromorphology of hardened paste. The results shoe and the strength of binding material, atch the standard of grade ordinary Portland cement. The hydration heat release characteristics of alkaliactivated steel slagslag based cementitious materials are similar to alkaliactivated slag cement, and the accumulative heat is limited. Steel slag and slag have a positive interaction, and the bination is beneficial to the development of the hydration process of the system.
Key entitious materials; alkali activated; hydration products
钢渣是炼钢时所产生的废渣,其产量约占粗钢产量的12%~15%.近年来,随着钢铁工业的发展,钢渣产量迅猛增长,2012年我国钢渣产量约为1亿t,但综合利用率只有10%左右[1],且多为低附加值的应用,如填埋、作路基等,大量钢渣被闲置堆积起来,对环境造成影响.
我国排放的钢渣大多为转炉钢渣,其化学和矿物组成都与水泥熟料相近,含有较多的C2S(硅酸二钙)和C3S(硅酸三钙).但钢渣的形成温度(1 650 ℃)较高,且多为自然冷却,常温活性很低,因此,被称为“过烧的水泥熟料”,具有潜在的胶凝活性[2].目前,多采用物理激发,化学激发等方法来激发钢渣活性,但是钢渣的化学成分波动较大,水化活性低,还可能产生安定性不良等问题[3-4],这些都限制了钢渣的实际应用.
研究发现钢渣与矿渣组合后,用水玻璃做激发剂能得到性能较好的胶凝材料[5].本文通过对碱激发钢渣矿渣胶凝材料(以下简称钢渣矿渣胶凝材料)强度的测试、反应过程水化热的测定、反应产物的XRD和SEM分析,.
1原材料及实验方法

实验用钢渣为莱芜钢厂的转炉钢渣,勃氏法测定比表面积476 m2/