该【含氟硅嵌段共聚物静电纺制备特殊浸润性表面的研究 】是由【wz_198613】上传分享，文档一共【3】页，该文档可以免费在线阅读，需要了解更多关于【含氟硅嵌段共聚物静电纺制备特殊浸润性表面的研究 】的内容，可以使用淘豆网的站内搜索功能，选择自己适合的文档，以下文字是截取该文章内的部分文字，如需要获得完整电子版，请下载此文档到您的设备，方便您编辑和打印。含氟硅嵌段共聚物静电纺制备特殊浸润性表面的研究 摘 要 含氟硅嵌段共聚物是一种应用广泛的高性能材料，其在静电纺制备特殊浸润性表面方面具有很好的应用潜力。本文以含氟硅嵌段共聚物为材料，通过静电纺技术制备特殊浸润性表面，并对其性能进行了研究和分析。结果表明，静电纺制备的含氟硅嵌段共聚物纤维具有良好的疏水、疏油性能，可广泛应用于防水、防污、防腐蚀等方面。 关键词：含氟硅嵌段共聚物；静电纺；浸润性表面 Abstract Perfluorosilicone block copolymers (PFES) are widely used high-performance materials with great potential for preparing special wettability surfaces by electrospinning. In this study, PFES was used as the material to prepare special wettability surfaces by electrospinning, and the properties were studied and analyzed. The results showed that the PFES fibers produced by electrospinning had good hydrophobic and oleophobic properties, which could be widely used in waterproofing, anti-pollution, and anti-corrosion applications. Keywords: Perfluorosilicone block copolymers; Electrospinning; Wettability surface 引言 在现代化社会中，防水、防污、防腐蚀等需求越来越大，如何制备具有特殊浸润性表面材料成为一个热门研究领域。含氟硅嵌段共聚物是一种应用广泛的高性能材料，其在制备特殊浸润性表面方面具有很好的应用潜力。同时，静电纺作为目前较为成熟的纤维制备技术，具有工艺简单、成本低、能够制备出直径微小的纤维等优点，广泛应用于过滤材料、医疗材料、传感器等领域。因此，本文选取含氟硅嵌段共聚物为材料，采用静电纺技术制备特殊浸润性表面，并对其性能进行研究分析。 实验部分 1 实验材料 含氟硅嵌段共聚物（PFES）；甲苯；氯仿；乙醇 2 实验仪器 静电纺纤维制备仪；扫描电镜；接触角仪 3 实验方法 合成含氟硅嵌段共聚物 将氟代硅烷单体和苯基硅烷单体按照一定的比例物质搅拌混合，并加入氯仿、甲苯、催化剂，并在150℃下恒温反应24h得到含氟硅嵌段共聚物。 静电纺制备含氟硅嵌段共聚物纳米纤维 将含氟硅嵌段共聚物在乙醇中溶解，制备出质量分数为9%的聚合物溶液。利用静电纺纤维制备仪进行静电纺纤维，，距离离心器30cm，辊筒转速60rpm，电极采用铝箔制成。 性能测试 利用接触角仪对不同含氟硅嵌段共聚物纤维进行水、乙醇、正十四烷的接触角测定，并利用扫描电镜对纤维进行形貌观察和尺寸分析。 结果与分析 图1为含氟硅嵌段共聚物静电纺制备的纳米纤维SEM图像，可以看出纤维比较细且表面比较光滑，平均直径为360nm左右。 图1 含氟硅嵌段共聚物静电纺制备的纳米纤维SEM图像 图2为不同含氟硅嵌段共聚物纤维与水、正十四烷、乙醇的接触角测定结果。可以看出PFES在水、正十四烷、°、°°，表现出了良好的疏水、疏油性能。 图2 不同含氟硅嵌段共聚物纤维与水、正十四烷、乙醇的接触角 结论 通过静电纺技术制备含氟硅嵌段共聚物纤维，可以制备出良好的疏水、疏油性能的纤维材料，可广泛应用于防水、防污、防腐蚀等方面。