温度对水泥的影响.doc

摘要
本文通过将水泥在不同温度下储存不同时间,然后测定其主要的物理性能,并且进行XRD、SEM的分析,研究水泥库中的温度和储存时间对水泥性能的影响。通过实验可以发现,普通硅酸盐水泥P·O ~100℃的温度范围内储存不同时间(1d、3d、5d、7d)时,与常温下储存的水泥相比,其标准稠度用水量、凝结时间基本没有变化,抗压抗折强度稍有提高,通过SEM发现水泥的矿物形貌和水化后的结构没有差别,通过XRD发现水泥中主要矿物的衍射峰也基本相同,只是C3S衍射峰稍有提高。说明当水泥库中的温度在70-100℃并且储存时间小于7d时,对水泥的性能基本是没有影响的。
关键词:温度;时间;物理性能;水泥库
ABSTRACT
In this paper we research the cement’s main physical property, after the cement is stored for different time at different analyse them by means of XRD and SEM,then we explore the influences of storage time and temperature for the cement in cement bunker. Compared with the cement who is stored at room temperature, we can find that the cement’s(P·O ) ,stored at 70-100℃for different days(1d、3d、5d、7d),the standard consistency water ,setting time has no change ,pression strength and rupture strength has increased slightly. We can find that mineral morphology of cement and hydration structure has no change by means of SEM and the main mineral in cement’s diffraction maximum is same by XRD,but C3S’s diffraction maximum increases. This indicates temperatures(70-100℃) and stored time(less than 7d) in cement bunker make no difference for cement greatly.
Key words: temperature; storage time; physical property; cement bunker
目录
摘要 I
ABSTRACT II
1前言 1
1
2
8
2 实验原料、设备及实验方法 10
10
原料性能 10
实验设备 10
11
12
12
12
微观结构分析 16
本章小结 17
3 环境温度和储存时间对于水泥性能的影响 18
18
18
20
20
23
XRD分析 25
扫描电镜分析 26
未水化水泥的扫描电镜分析 26
水泥水化的扫描电镜分析 27
本章小结 28
4 结论 29
参考文献 30
致谢 32
1前言

水泥是现代建筑行业的中一种极其重要的无机非金属材料,水泥工业的发展对保证的提高,具有十分重要的意义。
水泥从磨机出来之后,不可能直接装车,装船,或者用水泥袋子包装后出厂使用。基本上都需要先进入水泥库中进行储存,然后才可以出库使用。水泥库中心设有一大圆锥,库底圆锥周围的环行区被分成向库中心倾斜的六块扇形区,在每块扇形区内装有十条不同规格的充气箱,充气时水泥被送至其中两条径向布置的充气箱上,再通过圆锥体下部的出料口经充气卸料设备及卸料斜槽进入库底中央的均化仓。每个库底圆锥体下部至均化仓共有六套卸料系统。每套卸料系统由充气螺旋闸、气动开关