中厚板探伤不合原因分析及探讨.pdf

中厚板探伤不合原因分析及探讨
李伟 1 吴健鹏 1 徐静波 1 陈国威 2
(1 武汉钢铁(集团)公司制造部,武汉 430080;
2 武汉钢铁(集团)公司炼钢总厂二分厂, 武汉 430080 )

摘要通过对中厚板探伤不合部位取样进行金相、扫描电镜分析,探讨中厚板探伤不合的原因。研究结果表明:中厚板厚度
1/4和1/2处的微裂纹是引起探伤不合的主要原因。延长铸坯在炉停留时间和减弱连铸板坯的中心线偏析能够有效提高中厚板
的探伤合格率。
关键词中厚板探伤不合微裂纹偏析
Causes Analysis and Discussion of Detected Defects in Heavy
and Medium Plate

Li Wei1 Wu Jianpeng1 Xu Jingbo1 Cheng Guowei2
(1. Manufacture Department of WISCO , Wuhan 430080 ,China;
2. Brand of Steelmaking Plant of WISCO , Wuhan 430080 ,China)

Abstract The causes of detected defects in heavy and medium plate are analysed by ultrasonic inspection and SEM. The results
indicated detected defects are caused by micro-cracks in the pearlite band at the center area and 1/4 of the plate. Increasing the
heating furnace time and reducing the centerline segregation of the slabs could effectively improve the ultrasonic testing quality of
the plates.
Key words heavy and medium plate flaw detection micro-crack segregation
1 前言
中厚板被广泛的应用于建筑、石油、造船等工业中,作为结构件应用于高层建筑、大型压力容器、海
上石油平台、大型船舶等工程中,中厚板质量的好坏直接关系到这些项目的安全性和耐用性。目前,国内
外各大中厚板厂基本采用超声波探伤对中厚板的内部质量进行检验。
武钢炼钢总厂二分厂供给中厚板厂的连铸坯生产的中厚板,经常遇到超声波探伤不合的问题,特别是
压力容器系列钢,探伤合格率在一段时间均低于 90%,造成了大量的改判,并影响了交货期。本文就炼钢
总厂二分厂供给中厚板厂的连铸坯生产的中厚板出现的探伤不合钢板的内部缺陷进行研究,找出探伤不合
的原因,并提出一些解决的办法。
2 中厚板生产工艺流程及探伤统计
武钢的中厚板采用的工艺流程为:80t 转炉→RH→(900-1550mm)×(210、250)mm 板坯连铸机→
加热炉→双机架轧机→水幕→矫直机→冷床。