水热法制备Mn改性的ZnO纳米棒及其性质的研究.doc

水热法制备 Mn 改性的 ZnO 纳米棒及其性质
的研究
牛欣玥,李志杰,祖小涛
电子科技大学物理电子学院,四川成都 610054
摘要:采用尿素辅助的水热法直接了制备 Mn 改性的 ZnO 纳米棒。XRD 和 TEM 表明 ZnO
纳米棒为闪锌矿结构,直径在 200-400 nm 之间,长度为 2-3 µm。ZnO 纳米棒的表面覆盖有
一层氧化锰纳米颗粒,直径在 5-10 nm 之间。室温光致发光显示这种 Mn 改性的 ZnO 纳米棒
在 366 nm 和 382 nm 处出现的紫外发光和峰值为 490 nm,从 440 到 550 nm 的蓝光发光谱
带。其蓝光发光带峰值随着 Mn 添加量的增高发生红移,且明显增强。
关键词:ZnO, 水热法,纳米材料,光致发光
中图分类号:
Preparation and Properties of Manganese
Modified ZnO Nanorods by Hydrothermal
Process
NIU Xin-Yue,LI Zhi-Jie,ZU Xiao-Tao
School of Physical Electronics, University of Electronic Science and Technology of China,
Chengdu 610054 China
Abstract: Manganese oxide nanoparticles modified ZnO nanorods were prepared by
hydrothermal process. XRD and TEM analysis proved that the rods were sphalerite phase
structure, and the diameter of nanometer was 200-400 nm, the length was 2-3 micron. There
are manganese oxide nanoparticles on the surface of ZnO nanorods, which diameter is 5-10
nm. The room temperature photoluminescence showed there are two UV emissions and a
broad blue emission. With the increasing of Mn content, the blue emission red shifted and
increased.
Key words: ZnO, Hydrothermal, nanorod, photoluminescence
基金项目: 中央高校基本科研业务费专项资金(批准号:ZYGX2012J047)
作者简介: 牛欣玥(1988-),女,在读硕士研究生,主要研究方向:半导体材料,金属氧化物气敏传感器。通信作者:李志杰
(1974-),男,副教授,邮箱地址:******@uestc.,主要研究方向:纳米材料、纳米器件以及新型功能材料。
-1-
0 引言
一维纳米材料由于其在基础理论研究和潜在应用技术上的重要性近年来