钢箱梁桥用环氧沥青材料的制备马玉然 1 ,方坤 1 ,李依璇 2 ,熊金平 1* ( 1. 北京化工大学教育部碳纤维及功能高分子重点实验室, 北京化工大学北京市材料电化学过程与技术重点实验室,北京 100029 ; 2. 北京碧海舟腐蚀防护工业股份有限公司,北京 100029) 摘要: 本文以拉伸强度和断裂伸长率为主要考核指标, 通过正交试验优化出了环氧沥青材料的最佳配方, 在此基础上进一步研究了沥青、活性增容剂、固化剂等主要影响因素对环氧沥青材料力学性能的影响,所制备出的环氧沥青材料断裂伸长率高达 % 、拉伸强度 4 MPa 。关键词: 环氧沥青力学性能* 通讯作者: ******@. Preparation of epoxy asphalt materials used in steel bridge Yuran Ma 1, Kun Fang 1, Yixuan Li 2, Jinping Xiong 1* (1. Key Laboratory of Carbon Fiber and Functional Polymer of Education Ministry, Beijing Key Laboratory of Electrochemical Process and Technology for Materials, Beijing University of Chemical Technology, Beijing, 100029 2. Beijing Bihaizhou Corrosion and Protection Industry Co .Ltd , Beijing , 100029 ) Abstract : With the help of criterion of tensile strength and average elongation as evaluation the epoxy asphalt performance , the influences of the contents of asphalt, patibilizer, curing agents on the mechanical properties of the epoxy asphalt were studied by orthogonal experiments. The tensile strength and average elongation oft he optimized formula e poxy asphalt were % and , respectively . Key Words: E poxy A sphalt Mechanical Properties 1 、前言沥青因良好的矿物附着力和粘弹性而被广泛应用于铺设道路[1], 而较差的高低温性能导致其极易破坏而影响其使用性能。因此,对沥青进行改性以改善其性能来满足不同场合和环境条件下的使用需要势在必行。用环氧树脂来改性沥青是目前研究的热点之一。环氧树脂改性时, 加入沥青中的环氧树脂与固化剂发生的固化反应后形成网状结构固化物;而沥青分子将分散于这一环氧树脂的网状结构中,形成不可逆的固化物,从而赋予沥青以优