环氧沥青及混合料的制备与试验方法
杨幼江1 黄犀纯1 戚秉乾1 杨拯1 张彩龙1 王海涛1 张全敏2 王向圆2
401147; 030004
摘要:简要回顾环氧沥青混合料试验方法现状;环氧沥青原材料的制备与容留时间的确定;环氧沥青混合料的制备与检测方法,为环氧沥
青及混合料试验检测提供方法依据。
关键词:环氧沥青;混合料;容留时间;制备;试验方法
Epoxy asphalt and mixture preparation and test method
YANG You-jiang1,HUANG Xi-cun1,QI Bing-qian1,YANG Cheng1
ZHANG Cai-long1,WANG Hai-tao1,ZHANG Quan-min2,WANG Xiang-yuan
(1. Chongqing Road and Bridge Construction Fucheng FengShi Highway Overall Contracting Units,ChongQing 4011472
2. Shanxi Luxiang traffic science and Technology Consulting Co., Ltd.,Taiyuan 030004)
Abstract: A brief review of the status quo of test methods for epoxy asphalt mixture; Preparation and determine the reserved time of epoxy asphalt
materials; Preparation and detection method of epoxy asphalt mixture system, Method of providing basis for epoxy asphalt and its mixture test.
Key Words: Epoxy Asphalt; Mixture; Reserved Time; Preparation; Test Method
中图分类号:C35 文献标识码:A
1 绪论以初压作业)的时间称为环氧沥青混合料的最小容留时间;从
环氧沥青作为一种新型的桥面、路面铺装材料,近年来, 各混合料拌和到摊铺碾压(初压)困难(出现死料)的时间称
已在国内公路行业的多个领域得到推广和应用,特别是在水泥为环氧沥青混合料的最大容留时间。因此,施工过程中摊铺碾
混凝土桥面铺装工程中,已经得到了较为广泛的应用。但在室压施工时间应控制在最小和最大容留时间范围内完成。
内试验和现场施工过程中,环氧沥青混合料仍未形成一套完(2)容留时间的确定方法
整、规范的试验方法。本文从原材料和混合料的配制及试验检与普通沥青不同,环氧沥青材料自A、B组分混合后,会
测等方面对水泥混凝土桥面铺装用环氧沥青混合料的试验方法发生化学反应,其粘度随着时间、温度的增加而增长,容留时
进行系统研究。间的确定就是通过检测环