自硬呋喃树脂砂.doc

自硬呋喃树脂砂在高铬铸铁生产中的应用陈木林(湖北黄石东帆泵业有限公司湖北黄石 435006 ) 摘要: 介绍了自硬呋喃树脂砂在高铬合金铸铁生产中的实际应用。从原材料的选取,树脂砂的制备工艺,到采用该砂进行造型制芯的操作要点均作了较为详细的阐述。实践证明,采用自硬呋喃树脂砂生产高铬铸铁泵类过流件,可较好地满足其尺寸精度、表面光洁度要求,能有效地克服裂纹等铸造缺陷的产生。关键词: 自硬呋喃树脂砂高铬合金铸铁 Application of Self-setting Furan Resin Sand to High-chromium Iron Casting Production CHEN Mu-lin ( Hubei Huangshi Dongfan Pump Industry , Huangshi 435006, China) Abstract : The application of self-setting furan resin sand to high-chromium iron casting production has been discussed. In this paper the casting technique, in clouding the material choosing, resin sand preparation technology, operating rules of resin sand molding and coremaking, has been introduced. The production result shows that the casting size precision and surface smooth finish was increased and the crack defect was eliminated. Key words : self-setting furan resin sand; high-chromium iron casting 自硬呋喃树脂砂具有良好的工艺性能, 在铸造生产中得到了广泛地应用, 特别是在铸钢和普通灰口铸铁中应用较多, 在高铬合金铸铁件生产上的使用则相对较少,结合生产实践,本文予以介绍。 1 概况 1997 年以来, 我矿与清华大学合资成立泵业公司,专门从事开发生产新型固液两相流耐磨渣浆泵。泵用过流件材质大多为高铬铸铁, 而高铬铸铁属高合金铸铁, 铸造性能不同于一般普通铸铁和铸钢,其熔化和浇注温度高、收缩率大、导热性差、且在浇注过程中极易产生高熔点合金结膜而挂渣, 另外,过流件自身尺寸精度和表面光洁度要求较高, 采用普通粘土石英干型(芯) 砂铸造时, 铸件质量难以达标。经实践, 采用自硬呋喃树脂砂造型制芯后, 泵过流件质量明显改善, 铸件一次合格率提高 10~15% 。 2 原材料的选择与普通粘土砂相比, 自硬树脂砂具有其工艺上的特殊性, 对所用原材料要求较高, 因此, 应合理选材。 原砂的选择树脂砂对石英原砂的要求较高, 除了对化学成份有要求外,还必须严格控制含泥量、含水量、颗粒组成等,必要时,还应对酸耗值、表面状况、颗粒形状等指标进行控制。我们所选原砂的主要性能如下表 1: 表1 石英原砂的性能要求指标粒度 SiO