固溶处理对镁合金组织和耐腐蚀性能的影响.doc

摘要
论述了Mg-Al-Zn系合金经过固溶处理后组织和耐腐蚀性能的变化。通过观察经固溶处理后的组织及塔菲尔曲线,对Mg-Al-Zn系合金固溶处理后的组织和电化学腐蚀行为进行了研究。结果表明,经过固溶处理后的镁合金显微组织晶粒长大明显,β-(Mg17Al12)相部分溶解在基体组织中,在温度达到560度以上时,组织发生过烧现象。与未经处理镁合金的耐腐蚀性能相比,经过固溶处理后的镁合金耐腐蚀性能无明显增加。
关键词:镁合金;固溶处理;显微组织;耐腐蚀性能
Title: Solution Treatment on Mg-Al-Zn anizations and the impact of corrosion resistance
Abstract
Discusses the Mg-Al-Zn alloy after solution treatment and corrosion resistance after anization changes. By observing anization after solution treatment and the Tafel curves of Mg-Al-Zn alloy after solution treatment and electrochemical corrosion behavior was studied. The results showed that, after the magnesium alloy after solution treatment microstructure grain growth significantly, β-(Mg17Al12) phase partially dissolved in the anization, in the temperature reaches 560 degrees, the tissue over-burning phenomenon. With untreated corrosion resistance of magnesium pared to that after the magnesium alloy after solution treatment did not increase the corrosion resistance.
Keywords: Magnesium alloy;Microstructure;Corrosion resistance
目录
目录 3
第一章绪论 4
选题的目的与意义 4
镁合金 5
镁合金的发展 5
镁合金的性能及应用 6
镁合金在汽车上的应用: 6
镁合金在3C产品上的应用: 7
镁合金的种类及发展趋势 7
镁合金的种类 7
镁合金的发展趋势 8
合金元素对镁合金组织和力学性能的影响 10
镁合金主要化学成分 10
合金元素对合金组织和力学性能的影响 11
固溶处理的作用 13
固溶与时效处理 13
稀土镁合金 14
稀土镁合金的发展现状 14
稀土镁合金的开发应用及前景 15
本论文的主要研究内容 16
第二章试验方法及设备 17
实验选用材料 17
固溶处理实验所使用的材料 17
金相实验选用的材料 17
耐腐蚀实验所使用的材料 17
X射线衍射实验所使用的材料 17
实验方案 17
实验过程 19
固溶处理实验的过程 19
金相实验的过程 19
19
实验设备 20
第三章固溶处理对Mg-Al-Zn系镁合金显微组织的影响 22
AZ91D及AZ91D-RE合金的显微组织特征分析 22
AZ91D及AZ91D-RE镁合金固溶处理后显微组织特征分析 24
26
第四章固溶温度对Mg-Al-Zn系镁合金显微组织的影响 27
不同温度对Mg-Al-Zn系合金显微组织的影响 27
本章总结 31
第五章固溶时间对Mg-Al-Zn系镁合金显微组织的影响 32
不同时间对Mg-Al-Zn系镁合金显微组织的影响 32
本章结论 34
第六章固溶处理对Mg-Al-Zn系镁合金耐腐蚀性能的影响 35
固溶处理后冷却速度对AZ91D-RE系镁合金耐腐蚀性能的影