利多卡因膜剂的制备.doc

利多卡因膜剂的制备
赵惠玲
(广西中医药大学,广西南宁 530299)
摘要:目的掌握小量制备膜剂的方法;熟悉常用成膜材料的性质和特点。方法采用手工刮板法制备利多卡因外用膜剂。结果膜剂外观完整光洁,厚度一致,色泽均匀,无明显气泡。结论膜剂除主药和成膜材料,还需加入增塑剂(如甘油,山梨醇等)。
关键词:膜剂利多卡因成膜材料
Lidocaine perfect preparation
Zhao Huiling
(University of Chinese medicine in Guangxi, Guangxi Nanning 530299)
Abstract: objective to grasp the method of preparation the perfect small; Familiar with monly used properties and characteristics of film forming materials. Methods the scraper was prepared by hand lidocaine requests for external use only. The intact appearance bright and clean, the thickness is consistent, uniform color, no obvious bubbles. Conclusion in addition to the main drug and film-forming materials, the need to join plasticizer (such as glycerin, sorbitol, etc.). Keywords: preparing lidocaine film-forming materials
1仪器与材料
仪器玻璃板,玻璃棒,电磁炉等。
材料利多卡因,聚乙烯醇(PVA,1788),甘油,山梨醇,注射用水。
处方利多卡因 4g
PVA 4g
山梨醇
甘油
注射用水加至30ml
制法将PVA、山梨醇、甘油加适量水混匀,浸润溶胀后,加热至90摄氏度使溶解,加入研成极细粉的利多卡因,加水至全量,搅拌均匀后,在45摄氏度保温静置,除去气泡。将玻璃板预热至相同温度后,涂膜,,在70摄氏度干燥。
质量检查
外观检查
重量差异检查
取膜片20片,精密称定总质量,计算平均膜重后,再分别称定每片膜的质量。 2 实验结果 外观检查
制得的膜外观完整光洁,厚度一致,色泽均匀,无明显气泡。 重量差异检查
表一利多卡因膜剂重量差异检查结果
利多卡因膜剂
膜剂总重/g(20
片)
1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20