【2019年整理】吕厚为论文修改.docx

学士学位论文
论文题目：聚酰亚胺膜的制备
作 者： 吕厚为
指导教师姓名：胡知之
专业名称：化学工程与工艺
本实验以6FAP曲通过用不同次数重结晶的 CBD双不同回流次数的CBDA乍原料，DMAC 为原料在机械搅拌，冷水浴保护条件下合成聚酰胺酸（ PAA溶液，涂膜后通过热酰业 胺化方法得到聚酰业胺（PI）薄膜。然后，利用紫外-可见光谱（UV、红外光谱等方法 对PI膜材料的结构与性能进行表征，实验结果表明，经过重结晶的 CBDAS明性更好，
聚合度更加，性能更加优异。
关键词:CBDA;聚酰业胺； 结构与性能；薄膜
Abstract
In this paper, under the condition of mechanical agitation and the cold bath, we synthesized polyamide acid (PAA) solution with p-6FAPB and CBDA as raw material and DMAC as solvent, in which CBDA(cyclobutane dianhydride) was produced by photo-dimerization reaction, after coating we obtained polyimide(PI) film by thermal Imidization method. Then, we used ultraviolet-visible spectroscopy (UV), infrared spectrum method to characterize structures and properties of PI film. the experimental results show that PI film prepared by the CBDA from recrystallization have high transparency, more polymerization degree, and more excellent performance.
Keywords: CBDA; Polyimide; Structure and performance; film
摘 要 ii
ABSTRACT II
绪 论 IV
1聚酰亚胺简介 IV
VI
X I
.12
xvii
实验部分 xvii
XVII
xviii
XVIII
XIX
错误！未定义书签。
XX
反应原理.

： XXI
XXII

3 结果与讨论 xxii
xxii
XXII
-可见光谱 XXIII
结论 XXVI
致 谢 XXVI
参考文献 XXVII
附录 31
论


聚酰业胺是一类重要的高性能聚合物，由于其具有优异的热性能、力学性能、机械 性能和介电性能而广泛应用在航空航天、石油化工、现代微电子和光电子等领域 ［1,2］。
然而已商品化的聚酰业胺大多难溶难熔、加工性能差；而且制品颜色深，光学透明性差（在 接近500 nm时便有大量吸收）， 成具有良好溶解性能和光学透明性的聚酰业胺是一件十分有意义的研究工作 ［3~7］。基于
分子设计出发，近年来报道比较多的可溶性聚酰业胺是含氟聚酰酰业胺， 尤其是含有三
氟甲基取代结构的聚酰酰业胺［8~11］。它们通常是由含氟二胺单体和常见二酊单体缩聚得 到。由于聚合物分子主链中含有大的三氟甲基和柔性的酰键， 使得这类聚酰业胺通常表
现出较好的溶解性能；同时由于氟原子独特的物理化学性质， 如较大的电负性、较小的
原子半径、较低的摩尔极化率等，使得这类聚酰业胺还表现出较传统聚酰业胺更好的光
学性能、介电性能和低的吸湿率。
1908^, Bogert和Renshawffi过4-氨基邻苯二甲酸酊的熔融自缩聚，在实验室中首 次合成出了芳香型聚酰业胺[12]。由于当时高分子学科处于发展初期尚未从有机化学中分 离出来，对于聚合物的本质及其性能还没得到全面的认